1260T
September 8, 2024
It is an acrylic resin with active hydroxyl groups that is designed and manufactured to form a cross link with polyisocyanates, which is used for exterior coatings with good properties and high durability.
Main PropertiesFilm propertiesConsumption GuideSuggested UseStorage conditionsTechnical information
| Appearance | Clear liquid |
| Type of polymer | with the ability to form a cross link |
| Solvent | Xylene |
| Hazen color (APHA) (ASTM D-1209) Gardner (ASTM D-1544) | 50≥ |
| Solid percentage (ASTM D-1259) | 1 ∓ 55 |
| OH percentage (ASTM D-5155) | 1 |
| Acid number (mg KOH/g) (ASTM D-1639) | 5-10 |
| Viscosity at (cP) 25°C (ASTM D-562) | 1400-900 |
| Density at (g/ml) 25°C (ASTM D-1475) | 0.97 |
| Flash point (°C) (ASTM D-93) | 25 |
Good color and gloss durability • Excellent mechanical properties and good adhesion to various metals • Good outdoor durability and fast drying
• Used in combination with aliphatic polyisocyanates at ambient temperature or accelerated conditions. • The coatings reach their best properties after 10 to 12 days. But to speed up the hardening process, baking at 80 degrees Celsius for 30 minutes is suggested. Solvents such as alcohol and glycol should not be used. • Refer to the suggested formulas for additional information.
This resin with high adhesion ability on different surfaces and excellent flexibility is used to make lining and two-component topcoats resistant to atmospheric factors, water, detergents and chemicals. It is recommended to harden at room temperature or by applying heat.
Compatibility with other hydroxyl resins should be checked before use.
• Store in closed containers below 35 degrees Celsius in a well-ventilated place for up to 12 months.